Xometry.pro
en – Global
Knowledge & Community
Search
K
Quote & source your parts
Europe Europe
English DeutschFrançaisItalianoEspañol
Türkiye Türkiye
English Türkçe
United Kingdom United Kingdom
English
Global Global
English
select
navigate
switch tabs
Esc close

Get Instant Quote

Use our Instant Quoting Engine to easily quote and source your parts online

Get a Quote
Back
 Profile
Menu
Materials Library
Manufacturing Stories & Cases
AI Tools Directory
Articles
Free Tools
Ultimate 3D Printing Design Guide
E-books & Guides
Webinars
Community Discussions
Create Topic
Quote & Source Your Parts
Get a Quote

Edit topic

Home Xometry Community Materials & Finishes Why are my SLS PA 12 3D prints so brittle?

Why are my SLS PA 12 3D prints so brittle?

0
A
6

Hello, community! I have recently printed functional prototypes for snap-fit components using SLS with PA 12. The parts need to withstand repeated flexing without breaking. I noticed that the parts I’ve recently printed seem unusually brittle compared to previous batches and tend to crack or snap even under moderate stress. I haven’t made any design changes or material swaps between batches. Could this brittleness be caused by processing parameters or material degradation? Thnaks

Link copied
Solved by DanML

I see, then that is most likely the root cause of the issue, you need to mix in at least 50% fresh powder with SLS printers and 20% for MJF printers.

    • A

      Hello, community! I have recently printed functional prototypes for snap-fit components using SLS with PA 12. The parts need to withstand repeated flexing without breaking. I noticed that the parts I’ve recently printed seem unusually brittle compared to previous batches and tend to crack or snap even under moderate stress. I haven’t made any design changes or material swaps between batches. Could this brittleness be caused by processing parameters or material degradation? Thnaks

      0
      Reply
    • D

      Considering that you have not made any changes to the material or the design, it is indeed likely that some processing parameters or material degradation is the culprit. Are you using recycled powder in these recent prints and if so how much new powder do you usually mix in?

      0
      Reply
      Link copied
      • A
        DanML

        Yes I am using recycled powder, I don’t usually mix the new powder into the old powder, I usually take the old powder and just top it up with a small amount of new powder.

        0
        Reply
        Link copied
      • D
        Axl Hemmingway

        I see, then that is most likely the root cause of the issue, you need to mix in at least 50% fresh powder with SLS printers and 20% for MJF printers.

        0
        Reply
        Link copied
    • A

      Another potential cause is moisture ingress. PA 12 (Nylon) readily absorbs moisture, especially if it’s in powder form, you need to store your powder in a completely dry environment.

      0
      Reply
      Link copied
      • A
        Alex Bolt

        If I have left the powder exposed to a humid environment how can I go about drying the material out? Can I use an oven?If I have left the powder exposed to a humid environment how can I go about drying the material out? Can I use an oven?If I have left the powder exposed to a humid environment how can I go about drying the material out? Can I use an oven?

        0
        Reply
        Link copied
      • A
        Axl Hemmingway

        The material can be dried provided it has not absorbed too much moisture. I would advise against putting it in an oven to dry, you will most likely cause the powder to melt and bond together. The safest is to dry small batches using a desiccant dryer.

        0
        Reply
        Link copied
Why are my SLS PA 12 3D prints so brittle?
Your information:




Suggested Topics

Topic
Replies
Views
Activity
Contact
Materials & Finishes
Good day, I have been trying to receive the materials I paid for, for several days now. It's impossible to speak with anyone who can provide a serious and reliable update. The service is... read more
c
2
16
Aug 25
3D Printing
Materials & Finishes
Good morning, I would like a quote. I have attached some photos of 3D designs already created with AutoCAD as solids. I also have the DWG file that you can reference or use as... read more
l
3
68
Aug 20
Request for Material Information for Trumpet Mouthpiece
Materials & Finishes
Good day. I have a trumpet mouthpiece that I have modeled myself using FreeCAD, which I need to print. I conducted a small research and Google suggests using PETG (Polyethylene Terephthalate Glycol-modified) as a... read more
m
2
264
Jul 29
Teeth shearing off, what is the best material?
Materials & Finishes
Hello, we have this small tool used to loosen/tighten a metal slotted ferrule. The teeth of the tool engage with the slots in the ends of the ferrule and torque is applied to tighten... read more
a
1
928
Jun 26
Title: How to build a smartphone from scratch (parts & assembly) Description: Hello, I want to build a smartphone from scratch as a learning project. Can you please provide: – A full list of required components (mainboard, display, battery, cameras, etc.) – Recommended models or compatible parts – Estimated prices for each part – Step-by-step instructions on how to assemble them I am a beginner but I have basic experience with phone repair. Thank you!
Materials & Finishes
Title: How to build a smartphone from scratch (parts & assembly)Description:Hello, I want to build a smartphone from scratch as a learning project.Can you please provide:- A full list of required components (mainboard, display,... read more
0
991
May 05

Edit topic